Case material. Steel, nickel plated, or...?
« on: May 07, 2016, 01:27:33 PM »
I've got a lot of these, and I'm wondering if I can reload them.

Fly
Logged
Si vis pacem, para bellum

Offline shooter

  • NFOA Full Member
  • **
  • Join Date: Aug 2013
  • Location: near Yutan
  • Posts: 1630
Re: Case material. Steel, nickel plated, or...?
« Reply #1 on: May 07, 2016, 02:24:20 PM »
sure you can, those cases are just nickel plated brass cases. I load lead bullets in my brass, and jacketed in my nickel, just to keep it all the same    ( you can file off the nickel and see the brass underneath,)
Logged
Was mich nicht umbringt macht mich stärker
Sic semper evello mortem tyrannis
 NRA Endowment member
  Shoot  them in the crotch.  Clint Smith, thunder ranch.  Oct 14, 2016

Offline OnTheFly

  • Steel Benefactor
  • *
  • Join Date: Mar 2009
  • Location: Lincoln, NE
  • Posts: 2617
  • NFOA member #364
Re: Case material. Steel, nickel plated, or...?
« Reply #2 on: May 07, 2016, 09:15:45 PM »
You know, I could have just used a magnet to determine whether they are steel if I had thought of that earlier. DUH!

That's why they don't give me tools at work. Just $40,000,000 highly automated airplanes to fly.  ::)

Fly
« Last Edit: May 07, 2016, 09:18:01 PM by OnTheFly »
Logged
Si vis pacem, para bellum

Offline SemperFiGuy

  • Steel Benefactor
  • *
  • Join Date: Apr 2009
  • Location: Omaha, NE
  • Posts: 2079
  • GG Grampaw Wuz a DamYankee Cavalryman
Re: Case material. Steel, nickel plated, or...?
« Reply #3 on: May 08, 2016, 08:03:29 AM »
Tumble them enuf, soon the nickel plating will start to wear thin.

Eventually even be gone.   Worn off.

Then they're back to plain old ordinary everyday brass cases.

sfg
Logged
Certified Instructor:  NE CHP & NRA-Rifle, Pistol, Shotgun, Personal Protection Inside/Outside Home, Home Firearm Safety, RTBAV, Metallic Cartridge & Shotshell Reloading.  NRA Chief RSO, IDPA Safety Officer, USPSA Range Officer.  NRA RangeTechTeamAdvisor.  NE Hunter Education (F&B).   Glock Armorer

Offline Phantom

  • NFOA Full Member
  • **
  • Join Date: Feb 2012
  • Location: Omaha/Bellevue
  • Posts: 503
Re: Case material. Steel, nickel plated, or...?
« Reply #4 on: May 09, 2016, 01:48:56 PM »
Quote from: OnTheFly on May 07, 2016, 09:15:45 PM
That's why they don't give me tools at work. Just $40,000,000 highly automated airplanes to fly. 

Seems one could make a Joke here about "Playing with your joy stick all day long"  :o....but I won't make it   ;D :laugh:
Logged
"If the primates that we came from had known that someday politicians would come out of the...the gene pool, they'd a stayed up in the trees and written evolution off as a bad idea.....Hell, I always thought the opposable thumb was overrated.  "-- Sheridan, "Babylon 5"

Offline SS_N_NE

  • NFOA Full Member
  • **
  • Join Date: Feb 2012
  • Posts: 429
Re: Case material. Steel, nickel plated, or...?
« Reply #5 on: May 11, 2016, 09:14:26 PM »
Just a quick note about nickle plated brass: it has a rather limited reload life. The nickle plate will cause the brass to fail in fewer reloads than plain brass. Watch for cracking around the case mouth mostly in the crimp area. Sometimes sides just give up. Like anything else...results and opinion vary. It is particularly good for putting up some "emergency" reserve since the nickle plate will reduce corrosion (like a brass case..brown...green).
Logged